Boreetech's High-Hardness, No Tile-Breaking Transparent Polyaspartic Waterproof Coating is a two-component transparent waterproof adhesive designed specifically for high-strength waterproof repair. It uses polyaspartic resin as the core material, combined with isocyanate curing agent and a range of high-quality additives to deliver exceptional waterproof performance and high-hardness protection. With its light odor and excellent leveling properties, this product is ideal for no-tile-breaking waterproof repairs on floors and walls in both indoor and outdoor environments, especially on surfaces like tiles, glass, concrete, and metal, providing long-lasting protection.
Availability: | |
---|---|
Quantity: | |
Boree
Product Features
· Low Odor: Eco-friendly formula with minimal odor, making it suitable for indoor application without affecting the living environment.
· Excellent Leveling: The coating offers great leveling, resulting in a smooth surface, reducing construction defects and ensuring an aesthetically pleasing and protective finish.
· Extended Open Time: 30-60 minutes of open time ensures sufficient working time, making it suitable for larger construction areas.
· High Hardness: Once cured, the coating has high hardness, able to withstand heavy pressure and wear, making it suitable for high-traffic areas.
· Outstanding Waterproof Performance: Provides excellent waterproofing, effectively preventing water penetration for long-term protection.
Usage Instructions
The high-hardness, no tile-breaking transparent polyaspartic waterproof coating is suitable for waterproof repairs on various substrates, including tiles, concrete, glass, and metal. It allows for quick and simple repair without the need to damage existing floor or wall tile structures.
1. Surface Preparation: Ensure the substrate is dry, smooth, free from dust and grease, with a moisture content below 9%.
2. Mixing Ratio: Follow the prescribed mixing ratio for components A and B, stirring evenly to avoid air bubbles.
3. Application Process: One application is sufficient to achieve the desired effect. The thickness can be adjusted based on the flatness of the surface and protection requirements, typically between 0.15mm and 0.25mm.
4. Material Consumption Reference: Recommended usage is 0.2kg/m² to 0.3kg/m², adjustable based on the construction area and thickness.
Application Range
· Floor Waterproof Repair: Ideal for waterproof repairs in kitchens, bathrooms, balconies, and terraces, without breaking tiles.
· Wall Waterproof Repair: Suitable for interior wall leak repairs without damaging existing tiles or walls.
· Waterproof Coating Protection Layer: Can be used as a protective layer on various waterproof membranes to enhance durability.
Technical Parameters
· Main Agent Solid Content: ≥95%
· Curing Agent Solid Content: ≥96%
· Surface Drying Time: ≤6 hours
· Full Drying Time: ≤14 hours
· Tensile Strength: ≥10MPa
· Elongation at Break: ≥40%
· Bond Strength: ≥2.5MPa
Packaging and Storage
· Packaging Form: The product is packed in liquid bags and plastic buckets, with both the main agent and curing agent stored under nitrogen to prevent oxidation.
· Storage Conditions: Store in a cool, ventilated, and dry warehouse, avoiding contact with moisture and direct sunlight. The shelf life is 12 months from the production date.
· Transportation Requirements: Protect the product from rain, direct sunlight, and freezing during transportation. Ensure the product is not subjected to compression or impact to maintain its integrity.
Precautions
· It is recommended to apply a specialized primer before using this product to ensure better adhesion.
· Strictly follow the mixing ratio for components A and B and mix thoroughly to ensure optimal coating results.
· Opened components A and B should be used promptly, and any remaining unused parts must be sealed and stored in a cool place for immediate use.
· Ensure the construction site is well-ventilated, and avoid applying the product during rainy weather or on damp surfaces.
· The recommended application temperature is between 5°C and 35°C, and avoid working in environments with relative humidity above 75%.